Home » Residual Stress and Its Effects on Fatigue and Fracture: Proceedings of a Special Symposium Held Within the 16th European Conference of Fracture - Ecf16, Alexandroupolis, Greece, 3-7 July, 2006 by A.G. Youtsos
Residual Stress and Its Effects on Fatigue and Fracture: Proceedings of a Special Symposium Held Within the 16th European Conference of Fracture - Ecf16, Alexandroupolis, Greece, 3-7 July, 2006 A.G. Youtsos

Residual Stress and Its Effects on Fatigue and Fracture: Proceedings of a Special Symposium Held Within the 16th European Conference of Fracture - Ecf16, Alexandroupolis, Greece, 3-7 July, 2006

A.G. Youtsos

Published January 10th 2010
ISBN : 9781280901577
ebook
234 pages
Enter the sum

 About the Book 

Simplified fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineeringMoreSimplified fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabrication defects or cracks initiating and growing during service operation. Various procedures provide upper bound residual stress profiles for various classes of welded joints that can be used in fracture assessments, but these often give very conservative results. Recently, the option to use more realistic profiles has been adopted, but only where such profiles are based on finite element residual stress simulations supported by detailed residual stress measurements. Rapid advances in the capability of residual stress measurement techniques, such as the contour and deep hole drilling techniques as well as the neutron and synchrotron X-ray diffraction methods, now readily allow residual stresses and strains to be mapped on defined planes within a structure. The contents of this book have been grouped into three topic areas covering theoretical /numerical and experimental analyses of residual stress and its effects on fatigue and fracture.